LCP 7130L 美國杜邦公司 物性數據 |
|
①原料描述部分 |
|||||
|
②原料技術數據 |
|||||
|
性能項目 |
試驗條件[狀態] |
測試方法 |
測試數據 |
數據單位 |
|
|
物理性能 |
比重 |
黑色 |
ASTM D-792 |
1.62 |
--- |
|
泰伯摩擦 |
--- |
ASTM D-1044 |
63 |
mg |
|
|
?？s率 |
流向1.6mm |
ASTM D-955 |
-0.1 |
% |
|
|
?？s率 |
流向3.2mm |
ASTM D-955 |
0 |
% |
|
|
?？s率 |
橫向1.6mm |
ASTM D-955 |
0.9 |
% |
|
|
機械性能 |
?？s率 |
橫向3.2mm |
ASTM D-955 |
0.8 |
% |
|
洛氏硬度 |
Scale M |
ASTM D-785 |
63 |
--- |
|
|
沖擊下機械性能 |
--- |
UL 746B |
210 |
oC |
|
|
拉伸強度 |
23℃,1.6mm |
ASTM D-638 |
173 |
MPa |
|
|
拉伸強度 |
23℃,3.2mm |
ASTM D-638 |
150 |
MPa |
|
|
斷裂伸長率 |
23℃,1.6mm |
ASTM D-638 |
1.6 |
% |
|
|
斷裂伸長率 |
23℃,3.2mm |
ASTM D-638 |
1.7 |
% |
|
|
拉伸模量 |
23℃,1.6mm |
ASTM D-638 |
19306 |
MPa |
|
|
拉伸模量 |
23℃,3.2mm |
ASTM D-638 |
18000 |
MPa |
|
|
彎曲模量 |
23℃,0.8mm |
ASTM D-790 |
18000 |
MPa |
|
|
彎曲模量 |
23℃,1.6mm |
ASTM D-790 |
14000 |
MPa |
|
|
彎曲模量 |
23℃,3.2mm |
ASTM D-790 |
13100 |
MPa |
|
|
無缺口沖擊強度 |
23℃,1.6mm |
ASTM D-4812 |
840 |
j/m |
|
|
無缺口沖擊強度 |
23℃,3.2mm |
ASTM D-4812 |
555,20%NB |
j/m |
|
|
彎曲強度 |
23℃,0.8mm |
ASTM D-790 |
215 |
MPa |
|
|
彎曲強度 |
23℃,1.6mm |
ASTM D-790 |
192 |
MPa |
|
|
彎曲強度 |
23℃,3.2mm |
ASTM D-790 |
183 |
MPa |
|
|
壓縮強度 |
3.2mm |
ASTM D-695 |
89 |
MPa |
|
|
彎曲疲勞 |
3.2mm，69MPa |
ASTM D-671 |
2667 |
cycle |
|
|
IZOD沖擊強度 |
23℃,0.8mm |
ASTM D-256 |
400,40%NB |
j/m |
|
|
IZOD沖擊強度 |
23℃,1.6mm |
ASTM D-256 |
170 |
j/m |
|
|
IZOD沖擊強度 |
23℃,3.2mm |
ASTM D-256 |
225 |
j/m |
|
|
電氣性能 |
介電強度 |
1.6mm逐步 |
ASTM D-149 |
31 |
KV/mm |
|
介電強度 |
23℃,1.6mm短時間 |
ASTM D-149 |
35 |
KV/mm |
|