沙特基礎工業公司創新塑料 PEEK LNP* LUBRICOMP* LCL33 is a compound based on Polyetheretherketone resin containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Wear Resistant
LNP?LUBRICOMP? Compound LCL33 |
SI | | British | | Metric | Americas: COMMERCIAL |
| Also known as:LNP?LUBRICOMP?Compound LCL-4033 |
| Product reorder name:LCL33 |
| LNP LUBRICOMP LCL33 is a compound based on Polyetheretherketone resin containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Wear Resistant. |
|
Property |
| TYPICAL PROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, break | 1820 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, break | 1.7 | % | ASTM D 638 | |
| Tensile Modulus, 50 mm/min | 169400 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress | 2670 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus | 132100 | kgf/cm2 | ASTM D 790 | |
| Tensile Stress, break | 187 | MPa | ISO 527 | |
| Tensile Strain, break | 1.6 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 14700 | MPa | ISO 527 | |
| Flexural Stress | 276 | MPa | ISO 178 | |
| Flexural Modulus | 14700 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, unnotched, 23°C | 49 | cm-kgf/cm | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 6 | cm-kgf/cm | ASTM D 256 | |
| Instrumented Impact Energy @ peak, 23°C | 91 | cm-kgf | ASTM D 3763 | |
| Multiaxial Impact | 91 | cm-kgf | ISO 6603 | |
| Izod Impact, unnotched 80*10*4 +23°C | 34 | kJ/m2 | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m2 | ISO 180/1A | |
| THERMAL | Value | Unit | Standard | |
| HDT, 1.82 MPa, 3.2mm, unannealed | >298 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 2.34E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 4.14E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 2.36E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 4.17E-05 | 1/°C | ISO 11359-2 | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | >240 | °C | ISO 75/Af | |
| PHYSICAL | Value | Unit | Standard | |
| Density | 1.43 | g/cm3 | ASTM D 792 | |
| Moisture Absorption, 50% RH, 24 hrs | 0.07 | % | ASTM D 570 | |
| Mold Shrinkage, flow, 24 hrs (5) | 0.1 - 0.3 | % | ASTM D 955 | |
| Mold Shrinkage, xflow, 24 hrs (5) | 0.4 - 0.7 | % | ASTM D 955 | |
| Mold Shrinkage, flow, 24 hrs (5) | 0.1 - 0.3 | % | ISO 294 | |
| Mold Shrinkage, xflow, 24 hrs (5) | 0.3 - 0.7 | % | ISO 294 | |
| Wear Factor Washer | 13 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified | |
| Dynamic COF | 0.35 | - | ASTM D 3702 Modified | |
| Static COF | 0.28 | - | ASTM D 3702 Modified | |
| Density | 1.43 | g/cm3 | ISO 1183 | |
| Source GMD, last updated:2013/12/30 |
|
Processing |
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 150 | °C |
| Drying Time | 4 - 6 | hrs |
| Front - Zone 3 Temperature | 380 - 400 | °C |
| Middle - Zone 2 Temperature | 380 - 400 | °C |
| Rear - Zone 1 Temperature | 370 - 380 | °C |
| Mold Temperature | 175 - 190 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 60 - 100 | rpm |
| Source GMD, last updated:2013/12/30 |
|
美國液氮LNP LUBRICOMP PEEK LCL33E 碳纖維增強材料15%,PTFE潤滑劑 (15%) 美國液氮LNP LUBRICOMP PEEK LCL33 碳纖維增強材料15%,PTFE潤滑劑 (15%) 美國液氮LNP LUBRICOMP PEEK LCL33EXQ 碳纖維增強材料15%,PTFE潤滑劑 (15%) 美國液氮LNP LUBRICOMP PEEK LCL36 碳纖維增強,PTFE潤滑劑,導電 美國液氮LNP LUBRICOMP PEEK LCL36E 碳纖維增強,PTFE潤滑劑,導電 美國液氮LNP LUBRICOMP PEEK LL002 PTFE潤滑劑(10%) 美國液氮LNP LUBRICOMP PEEK LL003 PTFE潤滑劑(15%) 美國液氮LNP LUBRICOMP PEEK LL004 PTFE潤滑劑(20%) 美國液氮LNP LUBRICOMP PEEK LL004C PTFE潤滑劑(20%) 美國液氮LNP LUBRICOMP PEEK LL004E PTFE潤滑劑(20%) 美國液氮LNP LUBRICOMP PEEK LX00430 添加潤滑劑 美國液氮LNP LUBRICOMP PEEK LX82803 添加潤滑劑 美國液氮LNP LUBRICOMP PEEK LX91475 耐熱高335度 美國液氮LNP Stat-Kon* PEEK LX00797C 耐熱高335度 美國液氮LNP Stat-Kon* PEEK LX04420C 碳纖維增強導電 美國液氮LNP THERMOCOMP PEEK LC003E 碳纖維增強材料15% 美國液氮LNP THERMOCOMP PEEK LC004XXP 碳纖維增強20%,導電 美國液氮LNP THERMOCOMP PEEK LC006 碳纖維增強30%,導電 美國液氮LNP THERMOCOMP PEEK LC006EXQ 碳纖維增強30%,導電 美國液氮LNP THERMOCOMP PEEK LC008E 碳纖維增強材料, 40%,導電 美國液氮LNP THERMOCOMP PEEK LC008EXP 碳纖維增強導電 美國液氮LNP THERMOCOMP PEEK LC008EXQ 碳纖維增強材料40%,導電 美國液氮LNP THERMOCOMP PEEK LCF62E 玻璃纖維增強材料30%,碳纖維增強材料10% 美國液氮LNP THERMOCOMP PEEK LF002 玻纖維增強10% 美國液氮LNP THERMOCOMP PEEK LF003 玻纖維增強15% 美國液氮LNP THERMOCOMP PEEK LF004 玻纖維增強20% 美國液氮LNP THERMOCOMP PEEK LF004E 玻纖維增強20% |